Specially formulated to provide high definition molds. Ideal for printing hard objects but with compression capability. Specially formulated to model. Ideal for creating calcinable objects with great accuracy such as crowns, bridges and partial pieces. Developed to create jewelry pieces ready to be used for vulcanization. Created for jewelry prototypes that can be presented to customers and make custom adjustments.
This resin is ideal for creating objects in which a glassy finish without compression capacity under duress is desired. They show some contraction and are fast curing. Objects may not bend or widen under duress. They are characterized by high tensile and shear properties, high Vicat softening and little elongation.
SUMMARY TECHNICAL SPECIFICATIONS
At 25ºC Brookfield 230cPs
(After post exposure) 77 Shore D
ASTM D638 (After post exposure) 35 MPa
ASTM D638 (Before post exposure) 15 MPa
ASTM D638 (After post exposure) 2060 MPa
Elongation at break
ASTM D638 4%
Heat deflection temp
ASTM D648 60 ° C
Storage 10 <t> 50 ºC
Density 1.19 g / cm3